大型金属雕塑锻造工艺（2）
锻制的工艺过程比较简单，成型方法亦比较容易，它的圆雕和浮雕的锻造工艺制作方法是：
The forging process is relatively simple and the forming method is relatively easy. The forging process of the round carving and relief carving is made by:
首先做好泥塑，在泥塑的完成品上面翻阴模，阴模要求模具制作工艺材料要有一定的厚度，然后在外围用木枋形成统一的接触面，把阴模内的泥坯去掉，再用填充料进行模具修整，最后用铜质材料或不锈钢材料切割成各种不同形状的面，在阴模模具上直接敲打成型。
Firstly, do a good job of clay moulding. Turn over the negative moulds on the finished products of clay moulding. The negative moulds require certain thickness of the moulding process materials. Then, form a unified contact surface with wooden loquats on the periphery, remove the mud blanks in the negative moulds, and then use fillers to repair the moulds. Finally, use copper or stainless steel materials to cut into different types. The shape of the surface is directly tapped on the mould.
铜板材和不锈钢板材里面要有钢筋支撑。板材的选择厚度为0.4mm-2mm，铜板经过加热后具有很好的延展性，而不锈钢板是直接用来冷锻。
Copper plate and stainless steel plate should be supported by steel bars. The selected thickness of the sheet is 0.4mm-2mm. The copper sheet has good ductility after heating, while the stainless steel sheet is directly used for cold forging.
The forging process is relatively simple and the forming method is relatively easy. The forging process of the round carving and relief carving is made by:
首先做好泥塑，在泥塑的完成品上面翻阴模，阴模要求模具制作工艺材料要有一定的厚度，然后在外围用木枋形成统一的接触面，把阴模内的泥坯去掉，再用填充料进行模具修整，最后用铜质材料或不锈钢材料切割成各种不同形状的面，在阴模模具上直接敲打成型。
Firstly, do a good job of clay moulding. Turn over the negative moulds on the finished products of clay moulding. The negative moulds require certain thickness of the moulding process materials. Then, form a unified contact surface with wooden loquats on the periphery, remove the mud blanks in the negative moulds, and then use fillers to repair the moulds. Finally, use copper or stainless steel materials to cut into different types. The shape of the surface is directly tapped on the mould.
铜板材和不锈钢板材里面要有钢筋支撑。板材的选择厚度为0.4mm-2mm，铜板经过加热后具有很好的延展性，而不锈钢板是直接用来冷锻。
Copper plate and stainless steel plate should be supported by steel bars. The selected thickness of the sheet is 0.4mm-2mm. The copper sheet has good ductility after heating, while the stainless steel sheet is directly used for cold forging.